WATER-BASED SYSTEMS |
– |
FILM THICKNESS |
REALIZABLE SALT SPRAY HOURS |
1st RECOMMENDATION |
2nd RECOMMENDATION |
TO IMPROVE ADHESION (SYNERGY) |
ACRYLIC EMULSION PRIMER |
<15 microns |
100 hours |
HALOX® SZP-391 JM 3-5% & HALOX® 550 1-3% |
HALOX® 430 JM 3-5% & HALOX® 550 1-3% |
– |
>50 microns |
336 hours |
HALOX® SZP-391 3-5% |
HALOX® 750 3-5% |
HALOX® 570 LS or HALOX® 515 1-3% |
>50 microns |
500 hours |
HALOX® SZP-391 5% |
HALOX® 750 5% |
HALOX® 570 LS or HALOX® 515 1-3% |
ACRYLIC ELASTOMERIC COATINGS (ERC) – WHITE |
300-500 microns |
336 hours |
HALOX® CW-314 5-8% |
HALOX® SZP-391 5-8% |
HALOX® 570 LS or HALOX® 515 1-3% |
ACRYLIC ELASTOMERIC COATINGS (ERC) – PIGMENTED |
300-500 microns |
336 hours |
HALOX® CW-314 5-8% |
HALOX® SZP-391 5-8% |
HALOX® 570 LS or HALOX® 515 1-3% |
DIRECT-TO-METAL HIGH GLOSS ACRYLIC ENAMEL |
<25 microns |
100 hours |
HALOX® SZP-391 JM 1-3% |
HALOX® 430 JM 1-3% |
HALOX® 570 LS or HALOX® 515 1-3% |
>25 microns |
336-500 hours |
HALOX® SZP-391 3-5% |
HALOX® 430 3-5% |
HALOX® 570 LS or HALOX® 515 1-3% |
DIRECT-TO-METAL HIGH GLOSS ACRYLIC ENAMEL (Zinc free) |
80-90 microns |
336 hours |
HALOX® CW-314 3-5% |
HALOX® 430 JM 3-5% |
HALOX® 570 LS 1-3% or HALOX® FLASH-X 150® 1% |
ALKYD EMULSIONS & DISPERSIONS |
<25 microns |
100-200 hours |
HALOX® SZP-391 JM 3% & HALOX® 570 LS 1-3% |
HALOX® 430 JM |
HALOX® 550 WF or HALOX® 515 1-3% |
25-50 microns |
336 hours |
HALOX® SZP-391 1-3% & HALOX® 550 WF 1-3% |
HALOX® 750 3-5% |
HALOX® 570 LS or HALOX® 515 1-3% |
ALKYD EMULSIONS & DISPERSIONS (Zinc free) |
>50 microns |
500 hours |
HALOX® CW-314 2-3% |
HALOX® 430 JM 2-3% |
HALOX® 570 LS or HALOX® 550 1-3% |
2K POLYURETHANE |
<25 microns |
100-200 hours |
HALOX® 430 JM 1-3% |
HALOX® SZP-391 JM 5% |
HALOX® 570 LS 1-3% |
>25 microns |
336-500 hours |
HALOX® 430 3-5% |
HALOX® SW-111 3-5% |
HALOX® 570 LS 1-3% |
2K EPOXY |
<25 microns |
336 hours |
HALOX® 430 JM 1-3% |
HALOX® SZP-391 JM 1-3% |
HALOX® 550 WF 1-3% |
>25 microns |
500+ hours |
HALOX® SW-111 3-5% |
HALOX® 430 3-5% |
HALOX® 550 WF 1-3% |
2K EPOXY (Zinc free) |
45-50 microns |
1000 (CRS / Bonderite® 952) |
HALOX® CW-314 5-8% |
HALOX® SW-111 5-8% |
HALOX® 550 WF 1-3% |
1K EPOXY |
25+ microns |
68-336 hours |
HALOX® 750 5% or HALOX® 550 2% |
HALOX® SW-111 5% |
HALOX® 550 WF 1-3% |
EPOXY DISPERSION |
<25 microns |
336 hours |
HALOX® 430 JM 1-3% |
HALOX® SZP-391 JM 1-3% |
HALOX® 570 LS or HALOX® 515 1-3% |
>25 microns |
500+ hours |
HALOX® SW-111 5-7% |
HALOX® 750 5% |
HALOX® 570 LS or HALOX® 515 1-3% |
POLYVINYLIDENE CHLORIDE PVDC |
<25 microns |
200 hours |
HALOX® SZP-391 JM 1-3% |
HALOX® 430 JM 1-3% |
HALOX® 550 / 550 WF 1-3% |
PVDC (Rust Converter Primer) |
<25 microns |
48-168 hours |
HALOX® RC-980 |
HALOX® 550 WF 3-5% |
– |
CATIONIC ACRYLIC (pH<7) |
>50 microns |
72-100 hours |
HALOX® FLASH-X® 330 4-5% Pre-mix (1:1) with Water |
– |
HALOX® 550 1-2% |
CATIONIC ALKYD |
>50 microns |
200 hours |
HALOX® 550 / 550 WF 1-3% |
– |
– |
CATIONIC POLYURETHANE DISPERSIONS |
<50 microns |
>200 hours |
HALOX® FLASH-X® 330 4-5% Pre-mix (1:1) with Water |
– |
HALOX® 550 1-3% |
ANIONIC POLYURETHANE DISPERSIONS |
>50 microns |
<200 hours |
HALOX® 430 3-5% |
HALOX® 570 LS 1-3% |
HALOX® 550 1-3% |
1K CATIONIC EPOXY (pH<7) |
>50 microns |
100-500 hours |
HALOX® 391 5% |
HALOX® 430 JM 5% |
HALOX® 550 / 550 WF 1-3% |
HYBRID ACRYLIC ALKYD |
>50 microns |
<200 hours |
HALOX® 515 1-3% |
HALOX® 570 LS 1-3% |
HALOX® 550 / 550 WF 1-3% |
ACRYLIC EPOXY (Topcoat) |
>50 microns |
500+ hours |
HALOX® 570 LS or HALOX® 515 |
HALOX® 550 WF 1-3% |
– |
SILICONE EMULSION |
>50 microns |
200 hours |
HALOX® SZP-391 6-8% |
HALOX® 570 LS 1-3% |
HALOX® 550 WF 1-3% |
SILICONE ROOF COATINGS |
300-500 microns |
336-500 hours |
HALOX® CW-314 5-8% |
HALOX® SZP-391 5-8% |
HALOX® 570 LS or HALOX® 515 1-3% |
RUST PREVENTATIVE COATING (Temporary) |
<5 microns |
1-24 hours |
HALOX® 550 / 550 WF |
– |
SEE TDS |
PHENOLIC DISPERSIONS |
25-50 microns |
<500 hours |
HALOX® 391 3-5% or HALOX® 550 / 550 WF 1-2% |
HALOX® 750 3-5% |
– |